소형 인장시편을 이용한 TIG 용접된 이종금속 접합부의 변형 및 파괴거동 분석
신지환, Nabeel Jahanzeb, 김민성, 황지현, 최시훈
순천대학교 인쇄전자공학과
Analysis of Deformation and Failure Behaviors of TIG Welded Dissimilar Metal Joints Using Miniature Tensile Specimens
Ji-Hwan Shin, Nabeel Jahanzeb, Min-Seong Kim, Ji-Hyun Hwang, Shi-Hoon Choi
Department of Printed Electronics Engineering, Sunchon National University, Suncheon 57922, Republic of Korea
Correspondence  Shi-Hoon Choi ,Tel: +82-61-750-3556, Email: shihoon@sunchon.ac.kr
Received: 31 May 2016;  Accepted: 7 September 2016.  Published online: 2 February 2017.
The deformation and failure behaviors of dissimilar metal joints between SS400 steel and STS316L steel were investigated. The dissimilar metal joints were fabricated using the tungsten inert gas (TIG) welding process with STS309 steel as a filler metal. The microstructures of the dissimilar metal joints were investigated using an optical microscope and EBSD technique. The mechanical properties of the base metal (BM), heat affected zone (HAZ) and weld metal (WM) were measured using a micro-hardness and micro-tension tester combined with the digital image correlation (DIC) technique. The HAZ of the STS316L steel exhibited the highest micro-hardness value, and yield/tensile strengths, while the BM of the SS440 steel exhibited the lowest micro-hardness value and yield /tensile strengths. The grain size refinement in the HAZ of SS400 steel induced an enhancement of micro-hardness value and yield/tensile strengths compared to the BM of the SS400 steel. The WM, which consists of primary δ-ferrite and a matrix of austenite phase, exhibited relatively a high micro-hardness value, yield /tensile strengths and elongation compared to the BM and HAZ of the SS400 steel.
Keywords: metals, arc welding, fracture, electron backscattering diffraction(EBSD), digital image correlation(DIC)
PDF Links  PDF Links
Full text via DOI  Full text via DOI
Download Citation  Download Citation
Related article
Editorial Office
The Korean Institute of Metals and Materials
6th Fl., Seocho-daero 56-gil 38, Seocho-gu, Seoul 06633, Korea
TEL: +82-70-4266-1646   FAX: +82-2-557-1080   E-mail: metal@kim.or.kr
About |  Browse Articles |  Current Issue |  For Authors and Reviewers
Copyright © The Korean Institute of Metals and Materials. All rights reserved.                 Developed in M2Community