In-Jae Lee1, Sol-Bin Park1, Soon-Chul Ur1, Kyung-Wook Jang2, and Il-Ho Kim1,*
Thermoelectric Properties of MnSi1.74-1.75:Gem Prepared by Solid-State Reaction and Hot Pressing
Received: 2 January 2019;  Accepted: 25 February 2019.  Published online: 7 March 2019.
Higher manganese silicides (HMSs) MnSi1.74-1.75:Gem (m = 0.01–0.04) were prepared by solid-state reaction and hot pressing. The major phases of the HMSs were Mn27Si47 or Mn4Si7, and a small quantity of Si remained, but the intermetallic compound MnSi was not formed. The lattice constant increased with the substitution of Ge at Si sites. As the Ge content increased, the electrical conductivity increased, and the Seebeck coefficient decreased. The power factor was increased by Ge doping; however, the thermal conductivity also increased. Therefore, the dimensionless figure of merit (ZT) could not be increased significantly by Ge doping. For MnSi1.74:Gem, a maximum ZT of 0.36 was obtained at 823 K for MnSi1.74:Ge0.03; for MnSi1.75:Gem, a maximum ZT of 0.32 was achieved at 823 K for MnSi1.75:Ge0.01.
Keywords: thermoelectric, higher manganese silicide, HMS, doping, solid-state reaction, hot pressing
Editorial Office
The Korean Institute of Metals and Materials
6th Fl., Seocho-daero 56-gil 38, Seocho-gu, Seoul 06633, Korea
TEL: +82-70-4266-1646   FAX: +82-2-557-1080   E-mail: metal@kim.or.kr
About |  Browse Articles |  Current Issue |  For Authors and Reviewers
Copyright © The Korean Institute of Metals and Materials. All rights reserved.                 Developed in M2Community