Zn-Mg-Al 합금도금강판의 도장 내식성 및 밀착성(Corrosion Resistance and Adhesion of Paint Coating Film on Zn-Mg-Al Hot-Dip Galvanized Steel Sheets)
Received: 10 October 2018;  Accepted: 19 December 2018.  Published online: 9 January 2019.
Zn-Al-Mg alloy galvanized steel sheets have excellent corrosion resistance and improved cut-edge corrosion resistance. Most of the galvanized steel sheets used for outdoor applications are coated again on the galvanizing layer, or after a plastic film is laminated. As the corrosion products formed by the corrosion of Zn accumulate over time, the painting film blisters and peels, which causes a significant reduction in the value of the product. In this study, the coating adhesion and corrosion resistance of a Zn-Al alloy galvanized steel sheet with Mg added were evaluated by the salt spray test. The deterioraion of the coating film was also evaluated by Electrochemical Impedance spectroscopy(EIS) measurement. A quantitative evaluation of the coating film adhesion following water penetration between the plated layer and coating film under constant temperature and humidity condition was carried out using a Scanning Kelvin Probe(SKP).
Keywords: Zn-Al-Mg hot-dip galvanized steel sheets, paint coating film, corrosion, salt spray test, adhesion
PDF Links  PDF Links
Full text via DOI  Full text via DOI
Download Citation  Download Citation
Related article
Editorial Office
The Korean Institute of Metals and Materials
6th Fl., Seocho-daero 56-gil 38, Seocho-gu, Seoul 06633, Korea
TEL: +82-70-4266-1646   FAX: +82-2-557-1080   E-mail: metal@kim.or.kr
About |  Browse Articles |  Current Issue |  For Authors and Reviewers
Copyright © The Korean Institute of Metals and Materials. All rights reserved.                 Developed in M2Community