Abstract
The efficiency of gas turbines depends on the gas turbine working temperature. Single crystal blades are being applied more often than equiaxed blades in gas turbine engines, to increase the turbine inlet temperature, resulting in enhanced turbine engine efficiency. Single crystal blades endure creep conditions at high temperature better than..... More

Abstract
The influence of trace amounts of sulfur (S) on the microstructural evolution, tensile and creep properties in directionally solidified (DS) Ni-based superalloy GTD-111 were systematically investigated. Doping of S in the range of < 1 to 154 ppm resulted in the formation of a Ti₂SC-type carbosulfide phase near the coarse..... More

Abstract
In this study, the liquation cracking susceptibility in the heat-affected zone of CM247LC superalloy gas turbine blades during repair welding was quantitatively evaluated using a newly developed pre-weld Varestraint test method. The repair welding geometry was replicated through Varestraint tests for the pre-weld bead. The liquation cracking susceptibility, that is,..... More

Abstract
The metallurgical aspects of weld solidification cracking in Ni-based superalloys (with Ti+Al > 5 mass%) have not been widely investigated thus far. Herein, the solidification cracking susceptibility of the CM247LC superalloy and its welds with ERNiFeCr-2 filler wire was quantitatively evaluated using a novel modified Varestraint testing method, for the..... More

Abstract
The metallurgical aspects of weld cracking in Ni-based superalloys remain relatively unexplored in existing research. The present study performed comprehensive metallurgical and manufactural investigations into the weldability of an Ni-based superalloy, CM247LC, from the viewpoint of the liquation cracking behavior and its susceptibility. Metallurgical solutions to suppress the liquation-cracking susceptibility..... More

Abstract
In this study, the weldability of the as-cast CM247LC superalloy for turbine blade applications was metallurgically evaluated in terms of its hot cracking behavior and susceptibility. For this purpose, a real blade was manufactured using a directional solidification casting process, and gas tungsten arc welding was performed at the tip..... More