Evaluation of Liquation Cracking Behavior and Susceptibility in Heat-Affected Zone of CM247LC Superalloy Welds for Turbine Blade Application
CM247LC 초내열합금 터빈 블레이드 용접 열영향부의 액화균열 발생 거동 및 민감도 평가
Ye-Seon Jeong, Kyeong-Min Kim, Uijong Lee, Hyungsoo Lee, Seong-Moon Seo, Eun-Joon Chun
정예선, 김경민, 이의종, 이형수, 서성문, 천은준
Korean J. Met. Mater. 2020;58(12):875-886.   Published online 2020 Dec 4
DOI: https://doi.org/10.3365/KJMM.2020.58.12.875

In this study, the weldability of the as-cast CM247LC superalloy for turbine blade applications was metallurgically evaluated in terms of its hot cracking behavior and susceptibility. For this purpose, a real blade was manufactured using a directional solidification casting process, and gas tungsten arc welding was performed at the tip..... More

Effect of Electrode Patterning on Melting Behavior and Electrode Degradation in Resistance Spot Welding of A6014-T4 Alloy
A6014-T4 합금 소재의 저항 점 용접 시 용융 거동 및 전극 열화에 미치는 전극 패터닝 효과
Hyun-Uk Jun, Jae-Hun Kim, Jae Won Kim, Eun-Kyung Lee, Yang-Do Kim, Changwook Ji
전현욱, 김재훈, 김재원, 이은경, 김양도, 지창욱
Korean J. Met. Mater. 2020;58(12):863-874.   Published online 2020 Dec 4
DOI: https://doi.org/10.3365/KJMM.2020.58.12.863

In this study, the effects of electrode surface design on the resistance spot weldability and degradation of the electrode following resistance spot welding (RSW) of aluminum 6014-T4 alloy were investigated. A new patterning method that can be produced through repetitive pressurization was applied to the electrode, producing a lattice-like pattern..... More

Effect of Hot Stamping Heat Treatment Temperature on Resistance Spot Weldability of Al-10% Si Coated 30MnB5 Steel
핫스탬핑 열처리 온도가 Al-10% Si 도금 30MnB5 강의 점용접성에 미치는 영향
Seong Guk Son, Yeonjung Hwang, Chang Wook Lee, Ji Hong Yoo, Minsu Choi
손성국, 황연정, 이창욱, 유지홍, 최민수
Korean J. Met. Mater. 2019;57(12):778-786.   Published online 2019 Oct 8
DOI: https://doi.org/10.3365/KJMM.2019.57.12.778

Hot stamping is the most efficient manufacturing process to produce high strength automotive parts with reduced springback. Recently, 30MnB5 steel has been developed for hot stamping steel which can provide above 1700 MPa. However, resistance spot weldability of this steel is insufficient due to the need for a large amount..... More

Study on the Effect of the Localized Electrode Degradation on Weldability During an Electrode Life Test in Resistance Spot Welding of Ultra-High Strength Steel
초고강도강 저항 점용접 연속타점시 전극의 국부적 합금화 현상이 용접품질 저하에 미치는 영향 연구
Jae-Won Kim, Siva Prasad Murugan, Nam Hyun Kang, Yeong-Do Park
김재원, Siva Prasad Murugan, 강남현, 박영도
Korean J. Met. Mater. 2019;57(11):715-725.   Published online 2019 Nov 5
DOI: https://doi.org/10.3365/KJMM.2019.57.11.715

Evaluation of electrode degradation in resistance spot welding of 1180TRIP steel was carried out through an electrode life test, and weldability testing was performed by the measurement of the nugget size, the peak load analysis and the measurement of the electrode tip size at 30 intervals. Analysis of the change..... More

                           Cited By 1
Mechanical Performance and Microstructure of Resistance Element Welds of Dissimilar Metals Created with a Headless Rivet
Young Hyun Oh, Hyun Jung Ryu, Taejung Kim, Minsu Choi, Taeseon Lee
Korean J. Met. Mater. 2019;57(11):708-714.   Published online 2019 Oct 8
DOI: https://doi.org/10.3365/KJMM.2019.57.11.708

Resistance Element Welding (REW) is a novel processing technology developed to join dissimilar materials such as aluminum and steel. It uses an auxiliary steel rivet (element) inserted into an aluminum sheet that forms a resistance spot weld with the steel sheet, and the aluminum work piece is mechanically joined by..... More

                           Cited By 1
Study of the Corrosion Behaviour, Liquid Metal Embrittlement and Resistance Spot Weldability of Galvannealed Hot Stamping Steel
합금화 용융아연도금 핫스탬핑강의 자동차 차체 적용을 위한 부식 거동, 액상금속취화현상 및 점용접성 연구
Yeonjung Hwang, Chang Wook Lee, Ga-Young Shin, Ji Hong Yoo, Minsu Choi
황연정, 이창욱, 신가영, 유지홍, 최민수
Korean J. Met. Mater. 2019;57(3):193-201.   Published online 2019 Feb 8
DOI: https://doi.org/10.3365/KJMM.2019.57.3.193

The hot stamping process is beneficial for fabricating high strength automotive parts without spring back. To suppress high temperature oxidation and decarburization, it is necessary to coat the hot stamping steel. In the present work, the performance of galvannealed coated (GA) hot stamped steel was evaluated. During cyclic corrosion tests,..... More

                           Cited By 3
Impact Toughness and Softening of the Heat Affected Zone of High Heat Input Welded 390 MPa Yield Strength Grade TMCP Steel
항복강도 390 MPa급 가공열처리강 대입열용접 열영향부 충격인성 및 연화현상
Kook-Soo Bang, Young-Ho Ahn, Hong-Chul Jeong
방국수, 안영호, 정홍철
Korean J. Met. Mater. 2018;56(11):796-804.   Published online 2018 Nov 5
DOI: https://doi.org/10.3365/KJMM.2018.56.11.796

The Charpy impact toughness of the heat affected zone (HAZ) of electro gas welded 390 MPa yield strength grade steel, manufactured by a thermo mechanically controlled process, was investigated. The effects of added Nb on the toughness of the steel and the factors influencing scatter in toughness are discussed in..... More

                           Cited By 1
Evaluation on Reheat Cracking of Multi-pass Weld Metal of YP 690 QT Steel
해양플랜트용 YP 690 MPa급강 다층 용접부의 재열 균열 특성 평가
Yong Taek Shin, Young Ju Jo
신용택, 조영주
Korean J. Met. Mater. 2018;56(8):580-588.   Published online 2018 Aug 5
DOI: https://doi.org/10.3365/KJMM.2018.56.8.580

This study evaluated the relationship between reheat cracking that occurs in the reheated weld zone formed by subsequent multi-pass welding and the preheat/interpass temperature. The multi-pass weldment was YP 690 MPa high-strength steel, which is used in mobile offshore platform units. The welding process was flux-cored arc welding (FCAW), which..... More

Characterization of Microstructures and Creep Fracture Characteristics of Dissimilar Metal Welds between Inconel 740H Ni-Based Superalloy and Gr.92 Ferritic Steel
니켈기 Inconel 740H 초내열합금과 고Cr계 Gr.92 내열강의 이종금속 용접부의 미세조직 및 크리프 파단 특성
Kyeong-Yong Shin, Ji-Won Lee, Jung-Min Han, Kyong-Woon Lee, Byeong-Ook Kong, Hyun-Uk Hong
신경용, 이지원, 한정민, 이경운, 공병욱, 홍현욱
Korean J. Met. Mater. 2018;56(5):375-383.   Published online 2018 May 8
DOI: https://doi.org/10.3365/KJMM.2018.56.5.375

Microstructure evolution and the creep fracture characteristics of dissimilar welds between Ni-based superalloy Inconel 740H and High Cr ferritic steel Gr.92 were investigated. The dissimilar welds were fabricated by shielded metal arc (SMA) welding process with Ni-based austenitic Inconel 182 superalloy. Postweld heat treatment at 760 oC for 4 hours..... More

         Cited By 5
Effects of Welding Consumables on the Solidification Cracking in SAW Weld Metal of Medium Carbon Steel
중탄소강 SAW 용접금속의 응고 균열 발생에 미치는 용접재료의 영향
Kook-soo Bang, Woo-hyun Song, Hong-chul Jung
방국수, 송우현, 정홍철
Korean J. Met. Mater. 2018;56(2):137-145.   Published online 2018 Feb 5
DOI: https://doi.org/10.3365/KJMM.2018.56.2.137

The effects of submerged-arc welding consumables, wire and flux, on solidification cracking in the weld metal of medium-carbon steel were investigated. It showed that weld metal with a greater amount of C, S, and P had a wider brittleness temperature range, BTR, which resulted in longer total and maximum crack..... More

Effect of Aluminum Welding Wire Mg Content on the Mechanical Properties of Al 5083 Alloy Weld Metal
Al 5083 합금 용접부의 기계적 물성에 미치는 Mg의 영향
Dongyoon Kim, Dongcheol Kim, Munjin Kang, Young-Min Kim
김동윤, 김동철, 강문진, 김영민
Korean J. Met. Mater. 2017;55(10):716-723.   Published online 2017 Sep 28
DOI: https://doi.org/10.3365/KJMM.2017.55.10.716

A new aluminum welding wire with 0.8 wt% higher in Mg content was developed and compared with commercial welding wire of the 5000 series. The weldability of the Al5083 base material was evaluated using high current metal inert gas (MIG) welding, using the developed Al5183 and commercial Al5183 welding wire...... More

Evaluation of Mechanical Property for Welded Austenitic Stainless Steel 304 by Following Post Weld Heat Treatment
STS304의 후열처리에 따른 용접부 미세조직과 기계적 특성 평가
Daehan Jang, Kwangyoon Kim, Hyoung Chan Kim, Jong Bae Jeon, Dae-Geun Nam, Keun Yong Sohn, Byung Jun Kim
장대한, 김광윤, 김형찬, 전종배, 남대근, 손근용, 김병준
Korean J. Met. Mater. 2017;55(9):664-670.   Published online 2017 Aug 30
DOI: https://doi.org/10.3365/KJMM.2017.55.9.664

Austenitic stainless steels have excellent mechanical property and corrosion resistance, and are for these reasons used in demanding applications such as power plant, nuclear reactor and off-shore plant. Especially, austenitic stainless steel 304 (STS304) is mainly used as a pipe material in nuclear power plants. Submerged arc welding (SAW) is..... More

         Cited By 2
Growth Behavior of Intermetallic Compound in Dissimilar Al-Cu Joints Under Direct Current
알루미늄-구리 이종 도체 접합부에서 직류 전기 인가에 따른 금속간화합물의 성장 거동
Jeong-Ik Kim, Sung-woo Jin, Jinwook Jung, Hyun-Min Sung, Hye-Jin Jeong, Siwook Park, Ju-Won Park, Heung Nam Han
김정익, 진성우, 정진욱, 성현민, 정혜진, 박시욱, 박주원, 한흥남
Korean J. Met. Mater. 2017;55(6):372-378.   Published online 2017 Jun 1
DOI: https://doi.org/10.3365/KJMM.2017.55.6.372

Aluminum conductors are increasingly replacing copper because Al has lower cost and lighter weight, and consequently the demand for Al-Cu joints for industrial applications is growing. However, an intermetallic compound is known to grow at the Al-Cu interface, and will result in fracture if it grows above a critical thickness...... More

         Cited By 2
Effects of Nitrogen Content on the HAZ Softening of Ti-Containing High Strength Steels Manufactured by Accelerated Cooling
Ti 첨가 가속냉각형 고장력강의 용접열영향부 연화에 미치는 질소함량의 영향
Kook-soo Bang, Ho-shin Jung, Chan Park
방국수, 정호신, 박찬
Korean J. Met. Mater. 2017;55(3):191-197.   Published online 2017 Mar 3
DOI: https://doi.org/10.3365/KJMM.2017.55.3.191

The effects of nitrogen content on the HAZ softening of Ti-containing high strength steels manufactured by accelerating cooling were investigated and interpreted in terms of the microstructures in the softening zone. Regardless of their content, all of the steels investigated showed a softened zone 9-10 mm wide. The minimum hardness..... More

Analysis of Deformation and Failure Behaviors of TIG Welded Dissimilar Metal Joints Using Miniature Tensile Specimens
소형 인장시편을 이용한 TIG 용접된 이종금속 접합부의 변형 및 파괴거동 분석
Ji-Hwan Shin, Nabeel Jahanzeb, Min-Seong Kim, Ji-Hyun Hwang, Shi-Hoon Choi
신지환, Nabeel Jahanzeb, 김민성, 황지현, 최시훈
Korean J. Met. Mater. 2017;55(2):125-131.   Published online 2017 Feb 2
DOI: https://doi.org/10.3365/KJMM.2017.55.2.125

The deformation and failure behaviors of dissimilar metal joints between SS400 steel and STS316L steel were investigated. The dissimilar metal joints were fabricated using the tungsten inert gas (TIG) welding process with STS309 steel as a filler metal. The microstructures of the dissimilar metal joints were investigated using an optical..... More

         Cited By 3
Casting/Solidification/Heat Treatment
Microstructure and Mechanical Properties of Inconel 625 Alloy on Low Carbon Steel by Heat Treatment after Overlay Welding
저합금강의 인코넬 625 육성용접 후 열처리에 따른 미세조직 및 기계적 특성
Seungpil Kim, Jaeho Jang, Jungsoo Kim, Byung Jun Kim, Keun Yong Sohn, Dae-Geun Nam
김승필, 장재호, 김정수, 김병준, 손근용, 남대근
Korean J. Met. Mater. 2016;54(8):585-591.   Published online 2016 Aug 5
DOI: https://doi.org/10.3365/KJMM.2016.54.8.585
Overlay welding technique is one of methods used to improve metal mechanical properties such as strength, toughness and corrosion resistance. Generally, Inconel 625 alloy is used for overlay welding layer on low carbon steels for economic consideration. However, the method produces some problems in the microstructure of the cast structure... More
         Cited By 1
1 |
Email Alert
Author's Index
Impact factor
The Korean Institute of Metals and Materials
SCImago Journal & Country Rank
Similarity Check
Crossref Cited-by Linking
Editorial Office
The Korean Institute of Metals and Materials
6th Fl., Seocho-daero 56-gil 38, Seocho-gu, Seoul 06633, Korea
TEL: +82-2-557-1071   FAX: +82-2-557-1080   E-mail: metal@kim.or.kr
About |  Browse Articles |  Current Issue |  For Authors and Reviewers
Copyright © The Korean Institute of Metals and Materials. All rights reserved.                 Developed in M2PI